The construction method of thermal insulation mortar is briefly introduced in this paper.

1、保護層施工完畢后，養護2-3天（視氣溫而異）即可進行后序飾面層施工。

1. After the completion of the construction of the protective layer, the construction of the post-sequence decorative layer can be carried out after 2-3 days of maintenance (depending on the temperature).

2、熱天或基層干燥即可基層吸水量大時應用水濕潤，使基層達到內濕外干，表面無明水。

2. Hot days or base drying can be used to wet the base when the water absorption is large, so that the base can reach internal and external drying, and there is no clear water on the surface.

陜西保溫砂漿

Shaanxi thermal insulation mortar

3、基層表面應無粉塵和無油污及影響粘結性能的雜物。

3. There should be no dust and oil pollution on the surface of the base and impurities affecting the bonding performance.

4、將保溫系統專用界面劑按照水灰比1：4攪拌均勻，批刮于基層上，并拉成鋸齒狀，厚度約為3mm，或用噴涂方法也可。

4. The special interface agent for thermal insulation system is stirred evenly according to the water cement ratio of 1:4, scraped batch on the base, and pulled into serrated shape. The thickness is about 3mm, or spraying method can be used.

5、將無機保溫砂漿按照水灰比1：1攪拌成漿體，應攪拌均勻，無粉團。

5. Mixing inorganic thermal insulation mortar into slurry according to the ratio of water to cement 1:1, it should be stirred evenly and without powder.

6、后在抗堿網格布上再次涂抹2~3 MM厚度的抗裂砂漿。

6. Finally, the anti-cracking mortar with thickness of 2-3 MM is smeared on the anti-alkali mesh cloth.

陜西保溫砂漿廠家

Shaanxi thermal insulation mortar manufacturer

7、將抗裂砂漿涂抹于保溫砂漿上，厚度為2MM。

7. Apply anti-cracking mortar on insulation mortar with thickness of 2MM.

8、在抗裂砂漿表面掛上抗堿網格布。

8. Alkali-resistant mesh cloth is hung on the surface of crack-resistant mortar.

9、將保溫砂漿根據節能要求進行粉抹，2cm以上需分次施工，2遍抹灰間隔應在24小時以上，用噴涂方法也可以。

9. The insulation mortar should be whitewashed according to the requirement of energy saving. It needs to be constructed in stages above 2cm. The interval between two times of plastering should be more than 24 hours. Spraying method can also be used.